Helmet has hotspots.....massaging the EPS?
I have an HJC RPHA 90 modular helmet that I bought back in the spring. I've only worn it a couple times because I get hotspots on my forehead. I paid close to $500 for the lid so I'd lose a ton of money if I tried to sell it and buy something else. I thought about massaging the EPS. I've heard of others doing this with a soup can but I'm not sure if that's the best way or if there are any techniques others have found.
Any suggestions would be appreciated.
(P.S. Please spare me the public service announcements about how this will compromise the safety and integrity of the lid. I'm looking for a couple mm's, not an inch.)
HAGO!
-
Very Active Member
I've heard that a billiard ball could work OK. It's smooth, round, solid and easy enough to maneuver around the EPS. I have to track one down to try in the temple area of one of my helmets.
https://www.amazon.com/dp/B01E1OD01G...v_ov_lig_dp_it
2022 RT Sea To Sky
--------------------------------
-
Ozzie Ozzie Ozzie
Not that I'm recommending it or even making any sort of 'public service announcement', but surely it'd be better to 'ease' the hot spots by skimming & removing juust a little bit of the excess EPS in those areas with a dremel or similar, maybe even just giving it a go over with sandpaper?? That way, all the EPS that's left in those areas will still retain its original protective ability, lessened only by the tiny fraction due to the lesser depth; instead of compressing the whole depth of the EPS in those areas, cos you can't/won't be just compressing the top 1 or 2 millimetres of surface layer of EPS - due to its very nature you'll undoubtedly be compressing the entire depth of material and so losing a much larger percentage of compressibility in the material for its entire depth!!
After all, it's the compressibility that provides you with the impact protection, and if, as we are all warned about these types of helmets, simply dropping or knocking the helmet hard enough is able to reduce the protection it provides by compressing/collapsing the EPS, then having juust a millimetre or two less but still the same compression rate for all that remains has surely got to be better than having less compression rate for the entire depth & therefore less protection for the entire thickness of the EPS over what is likely to be your most vulnerable spots?!
And I know that many 'professional race helmets' have been/are given their 'final tuning' of their custom fitting by carefully shaving out very thin slivers of EPS rather than compressing it to ease the hot spots, so I'd guess there's a pretty good reason for doing it that way?!
Just sayin'
Last edited by Peter Aawen; 09-23-2020 at 08:53 AM.
2013 RT Ltd Pearl White
Ryde More, Worry Less!
-
Very Active Member
I use a large spoon from wife's kitchen to massage my HJC helmets in the forehead location. I like HJC, but recently switched to Shoei when I found one that fits my head perfectly. All heads are not created equally.
-
Good suggestions, all. I appreciate it.
Navydad---I have a Shoei J-Cruise (v1) that I LOVE. It fits almost perfectly however since it's a 3/4 lid, it's noisy and since I ride year round, not perfect for cooler weather. I seriously considered selling the HJC and buying a new Shoei Neotech 2 but it's $700, the proprietary com system is another $300 and the HJC is paid for.
HAGO!
-
Very Active Member
Originally Posted by Peter Aawen
Not that I'm recommending it or even making any sort of 'public service announcement', but surely it'd be better to 'ease' the hot spots by skimming & removing juust a little bit of the excess EPS in those areas with a dremel or similar, maybe even just giving it a go over with sandpaper?? That way, all the EPS that's left in those areas will still retain its original protective ability, lessened only by the tiny fraction due to the lesser depth; instead of compressing the whole depth of the EPS in those areas, cos you can't/won't be just compressing the top 1 or 2 millimetres of surface layer of EPS - due to its very nature you'll undoubtedly be compressing the entire depth of material and so losing a much larger percentage of compressibility in the material for its entire depth!!
After all, it's the compressibility that provides you with the impact protection, and if, as we are all warned about these types of helmets, simply dropping or knocking the helmet hard enough is able to reduce the protection it provides by compressing/collapsing the EPS, then having juust a millimetre or two less but still the same compression rate for all that remains has surely got to be better than having less compression rate for the entire depth & therefore less protection for the entire thickness of the EPS over what is likely to be your most vulnerable spots?!
And I know that many 'professional race helmets' have been/are given their 'final tuning' of their custom fitting by carefully shaving out very thin slivers of EPS rather than compressing it to ease the hot spots, so I'd guess there's a pretty good reason for doing it that way?!
Just sayin'
I did that method for some comm speaker pockets in a couple of helmets to get them a touch deeper. That EPS is MESSY and flies everywhere
2022 RT Sea To Sky
--------------------------------
-
Ozzie Ozzie Ozzie
2013 RT Ltd Pearl White
Ryde More, Worry Less!
-
Very Active Member
Dremel tool????
Originally Posted by Peter Aawen
Not that I'm recommending it or even making any sort of 'public service announcement', but surely it'd be better to 'ease' the hot spots by skimming & removing juust a little bit of the excess EPS in those areas with a dremel or similar, maybe even just giving it a go over with sandpaper?? That way, all the EPS that's left in those areas will still retain its original protective ability, lessened only by the tiny fraction due to the lesser depth; instead of compressing the whole depth of the EPS in those areas, cos you can't/won't be just compressing the top 1 or 2 millimetres of surface layer of EPS - due to its very nature you'll undoubtedly be compressing the entire depth of material and so losing a much larger percentage of compressibility in the material for its entire depth!!
After all, it's the compressibility that provides you with the impact protection, and if, as we are all warned about these types of helmets, simply dropping or knocking the helmet hard enough is able to reduce the protection it provides by compressing/collapsing the EPS, then having juust a millimetre or two less but still the same compression rate for all that remains has surely got to be better than having less compression rate for the entire depth & therefore less protection for the entire thickness of the EPS over what is likely to be your most vulnerable spots?!
And I know that many 'professional race helmets' have been/are given their 'final tuning' of their custom fitting by carefully shaving out very thin slivers of EPS rather than compressing it to ease the hot spots, so I'd guess there's a pretty good reason for doing it that way?!
Just sayin'
I've done this a few helmets to make them fit MUCH better. Not loose , just a better fit. I also aliened the top vent holes in my current helmet as VERY poorly aliened. Works much better now. Yes messy, but easily cleaned up with air pressure.
Lew L
Kaos----- Gone but not forgotten.
2014 RTS in Circuit Yellow, farkle-ing addiction down to once every few months. ECU FLASH IS GREAT.
-
Very Active Member
I used a ball peen hammer. Worked well.
I have an oval head and bought LS2 for 75.00 works well.
Get this the cheaper helmet has a shatterproof shield the HJC doesn't Imagine that
-
Very Active Member
Originally Posted by MONK
Good suggestions, all. I appreciate it.
Navydad---I have a Shoei J-Cruise (v1) that I LOVE. It fits almost perfectly however since it's a 3/4 lid, it's noisy and since I ride year round, not perfect for cooler weather. I seriously considered selling the HJC and buying a new Shoei Neotech 2 but it's $700, the proprietary com system is another $300 and the HJC is paid for.
HAGO!
Shoei GT-Air full face. A bit tight going on or off, but all day comfortable.
-
Originally Posted by Navydad
Shoei GT-Air full face. A bit tight going on or off, but all day comfortable.
I'm claustrophobic so I don't do full face helmets. Good suggestion, though.
-